Highcraft Clevis Hanger absorbs shock, anchors, guides and carries the load of stationary pipe lines. With High craft-standard quality and specialty clevis features, it is the ideal choice for your pipe line needs.
Clevis Features
Pivoting Bottom Accommodates Minor Pipe Vibration / Clevis Pin Allows 15° Swing Right And Left / Vertical Hanger Position Can Be Adjusted Up And Down Before And After Installation
Specifications
- Fits Pipe 14 In. / Fits Rod 1 In. / Max Load 4200 / Max Temperature 650° F
Variants
Copper Epoxy Coated
This coating provides excellent resistance to chipping, peeling, and corrosion. This coating is also an excellent base should the part need to be painted or powder coated before or after installation.
Epoxy Coated
Epoxy powder coating is applied electrostatically after fabrication as a free-flowing, dry powder. Once the product is pre-treated and clean, it is coated with the powder. It proceeds through a baking process creating a chemical bond and is finished by curing under heat to form a "skin".
Electro Galvanized
Electro-galvanized process deposits zinc on the surface of the steel or iron by electrolysis from a bath of zinc salts. The thickness of zinc applied in this method is between 0.2 mils to 0.5 mils [5.1 μm to 12.7 μm] and meet ASTM B633. EG finish is usually recommended for indoor use in relatively dry areas.
Galvanized
Pre-galvanized zinc is produced by hot dipping the steel coil or sheet through molten zinc at the mill prior to fabrication. This is also known as "mill galvanized" or "hot-dipped mill galvanized" Coils are then slit to size for fabrication of the finished product.
Plastic Coated
Products in this finish are plastic or vinyl coated for prevention of galvanic reaction between materials or for noise reduction. These coated products can also be used where contact between glass pipe and hanger is not desirable
Plain
The plain finish designation means that the product retains the oiled surface applied to the steel prior to the rolling process. This method offers no protection from corrosion.